2.5mm-15.5mm Hot Rolled Carbon Steel Ms Sheet Medium Carbon Alloy
Steel Plate
| Products | Corten Steel Plate |
Standard
grade | ASTM: Corten A; Corten B; A588Gr.A/Gr.B/Gr.C/ Gr.K; A242; A606 Type
4;
A709 Gr 50W; |
|
EN10025: S235J0W; S235J2W; S355J0W; S355J2W; S355K2W; S355J0WP;
S355J2WP; S355J2G1W; S355J2G2W; S355K2G1W, S355K2G2W; |
|
|
JIS G3114: SMA400AW; SMA400BW; SMA400CW; SMA490AW; SMA490BW;
SMA490CW; SMA570W; SMA570P; |
|
|
| JIS G3125: SPA-H; SPA-C; |
GB/T 4171: Q235NH; Q265GNH; Q310GNH; Q295NH; Q295GNH;
Q355NH;Q355GNH;
Q415NH; Q460NH; 1500NH; Q550NH; |
|
| TB/T 1979: 09CuPCrNi-A; 09CuCrNi-B; 05CuPCrNi; |
| Q/BQB 340: B460NQR; B490NQR; B480GNQR; B600GNQR; |
| Thickness | Cold Rolled 0.5-2mm Hot Rolled 2-300mm (2-100mm usually used) |
| Width | 1000-3000mm (1000-2200mm usually used) |
| Length | 1000-12000mm or as your request |
| Surface | Clean, finishing,blasting and painting according to customer
requirement |
| Process | Hot-rolled, Controlled rolling, Normalizing, Annealing, Tempering,
Quenching, N+T, Q+T,
and other delivery states are available as required |
|
| Certificate | API,ISO,SGS,BV,CE etc |
| Quality | MTC will be provided with goods, third part inspection is
acceptable,
for example BV,SGS. |
|
| Package | Standard export seaworthy package,suit for all kinds of
transport,or as required. |
| Container Size | 20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) |
| 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) |
| Trade term | Ex-Work,FOB,CNF,CFR,CIF,etc |
| Application | Widely used in a variety of architectural and engineering
structures,such as |
| 1.) metal constructions such as buildings,bridges,ships; |
| 2.) transmission tower, reaction tower; |
| 3.) lifting transportation machinery; |
| 4.) industrial furnace;boilers |
| 5.) container frame, warehouse goods shelves, etc |
Causes and effects of normalizing, tempering and quenching of
carbon steel plates
Normalizing: Normalizing is a heat treatment to improve the
toughness of steel. The steel member is heated to 30 ~ 50℃ above
the Ac3 temperature, and then it is cooled by air for a period of
time. The main characteristic is that the cooling speed is faster
than annealing but lower than quenching, normalizing can make the
steel crystal grain refinement in slightly faster cooling, not only
can get satisfactory strength, but also can obviously improve the
toughness (AKV value), reduce the cracking tendency of the
component.
Two, tempering: tempering is a heat treatment process in which the
workpiece is heated to a certain temperature below Ac1 (the
beginning temperature of pearlite to austenite transformation when
heated) after hardening. It is kept for a certain time and then
cooled to room temperature.
Tempering is generally followed by quenching, with the purpose of:
(a) Eliminate residual stress generated during quenching of the
workpiece to prevent deformation and cracking;
(b) Adjust the hardness, strength, plasticity and toughness of the
workpiece to meet the performance requirements;
(c) Stable organization and size to ensure accuracy;
(d) Improvement and enhancement of machining performance.
Therefore, tempering is the last important step in obtaining the
desired performance of the workpiece. Through the combination of
quenching and tempering, the desired mechanical properties can be
obtained.
According to the tempering temperature range, tempering can be
divided into low temperature tempering, medium temperature
tempering and high temperature tempering.
Three, quenching: workpiece heating austenitizing after cooling in
an appropriate way to obtain martensite or bainite structure of
heat treatment process. The most common are water-cooled quenching,
oil-cooled quenching, air-cooled quenching and so on.
Annealing, normalizing, quenching and tempering are the "four
fires" in the whole heat treatment. The quenching and tempering are
closely related to each other and are often used together.