Grade : NM360, NM400, NM500, NM550,
WNM360, WNM400, WNM450, WNM500 |
Thickness : 8mm-150mm
Width : 1000mm-4000mm
Length : 1000mm-20000mm |
MOQ: 1 PC
Product type : Steel plate
Delivery time : Promptly ( Stock) or 10-40 days (Production)
Payment Terms: L/C, T/T, etc
Stock : Available
MTC: Available |
| Delivery condition: Q+T |
Steel grades and chemical composition(MAX, %):
| C | SI | MN | P | S | CR | NI | MO | TI | B | ALS |
| NM300 | 0.23 | 0.70 | 1.60 | 0.025 | 0.015 | 0.70 | 0.50 | 0.40 | 0.050 |
0.0005-0.006
|
0.10 |
NM360 | 0.25 | 0.70 | 1.60 | 0.025 | 0.015 | 0.80 | 0.50 | 0.50 |
| NM400 | 0.30 | 0.70 | 1.60 | 0.025 | 0.010 | 1.00 | 0.70 | 0.50 |
| NM450 | 0.35 | 0.70 | 1.70 | 0.020 | 0.010 | 1.10 | 0.80 | 0.55 |
| NM500 | 0.38 | 0.70 | 1.70 | 0.020 | 0.010 | 1.20 | 1.00 | 0.65 |
| Tensile strength(MPa) | Elongation(%) | (-20)AKV(J) | Hardness(HB) |
| NM300 | 1000(min) | 14(min) | 24(min) | 270-330 |
| NM360 | 1100(min) | 12(min) | 24(min) | 330-390 |
| NM400 | 1200(min) | 10(min) | 24(min) | 370-430 |
| NM450 | 1250(min) | 7(min) | 24(min) | 420-480 |
| NM500 | -- | -- | -- | 470(min) |
wear resistant steel plate
wear resistant steel plate is a high-carbon alloy steel designed
specifically to have greater hardness properties than low-carbon
steel.
Hardness typically comes at the expense of strength, making AR
wear-resistant steel an ideal material for harsh, high-abrasion
conditions, and not for structural applications.
Material:
Sweden : 400 wear resistant steel plate, 450 wear resistant steel
plate, 500 wear resistant steel plate, 550 wear resistant steel
plate, 600 wear resistant steel plate.
Germany:XAR 400 wear resistant steel plate,XAR 300 wear resistant
steel plate,XAR 500 wear resistant steel plate
Dillidur400 wear resistant steel plate,Dillidur 500 wear resistant
steel plate,
Frace:Creusabro4800 wear resistant steel plate,Creusabro 8000 wear
resistant steel plate
high strength steel plate
High-strength steel plate (high-strength plate) has high strength,
especially in the normalizing or normalizing and tempering state,
it has higher comprehensive mechanical properties. Mainly used for
large ships, bridges, power station equipment, medium and high
pressure boilers, high pressure vessels, rolling stock, hoisting
machinery, mining machinery and other large welded structural
parts.
Corten steel plate
Weathering steel, often referred to by the genericised trademark COR-TEN steel and
sometimes written without the hyphen as corten steel, is a group of steel alloys which were developed to eliminate the
need for painting, and form a stable rust-like appearance after
several years' exposure to weather.
U.S. Steel holds the registered trademark on the name COR-TEN. The
name COR-TEN refers to the two distinguishing properties of this
type of steel: corrosion resistance and tensile strength.Although
USS sold its discrete plate business to International Steel Group
(now ArcelorMittal) in 2003, it still sells COR-TEN branded
material in strip-mill plate and sheet forms.
The original COR-TEN received the standard designation A242
(COR-TEN A) from the ASTM International standards group. Newer ASTM
grades are A588 (COR-TEN B) and A606 for thin sheet. All alloys are
in common production and use.
The surface oxidation of weathering steel takes six months, but
surface treatments can accelerate the oxidation to as little as two
hours